Dacromet ti a bo hexagonal cylindrical head skru: Boluti kekere kan pinnu igbesi aye awọn ohun elo ti o tobi, ipata-ipata ati sooro ipata, ati pe ko si eewu ti o farapamọ ti embrittlement hydrogen.

2026-11-04

1. Ifaara: Bolt ti o mu Awọn ẹrọ papọ

Rin nipasẹ eyikeyi ile itaja ẹrọ, sẹẹli roboti, tabi afẹfẹ-turbine nacelle ati pe iwọ yoo rii imuduro kanna: screw cylindrical-head screw with a hexagonal recess, tightened with all Allen bọtini. Eyi ni hexagon iho ori fila dabaru, Idiwọn bi DIN 912 ati ISO 4762. O jẹ boluti aiyipada fun awọn apẹrẹ ti o ku, awọn irinṣẹ ẹrọ, awọn ẹrọ hydraulic, ati awọn apejọ ti o tọ, nitori pe o ṣojuuwọn fifuye dimole giga ni apoowe iwapọ ati pe o le tun pada sinu counterbore.

2. Itumọ Ọja: Hexagon Socket Head Cap Screw

Jiometirika ti boluti yii jẹ iṣapeye fun iṣaju, kii ṣe fun irisi didan:

Silindrical oripẹlu oju didan alapin ti o pin ẹru dimole lori agbegbe ipin ni kikun.
Ti abẹnu hexagon iho(metric kọja-alapin lati 2.5 mm to 36 mm), gbigbe iyipo nipasẹ mefa oju pẹlu pọọku Kame.awo-jade.
Okun metric ti o ni kikun(isokuso tabi ipolowo ti o dara fun ISO 261), yiyi kuku ju ge fun ṣiṣan ọkà lilọsiwaju ati igbesi aye rirẹ to dara julọ.
Awọn kilasi ohun-ini 8.8, 10.9, ati 12.9, ibora ti awọn agbara fifẹ lati 800 si 1,220 MPa.

Opo	Ori Dia. (dk)	Giga ori (k)	Hex Socket (awọn)	Kilasi 8.8 fifẹ	Kilasi 12.9 fifẹ	Awọn ipari ti o wọpọ
M5	8,5 mm	5.0 mm	4 mm	800 MPa	1.220 MPa	10-60 mm
M6	10.0 mm	6.0 mm	5 mm	800 MPa	1.220 MPa	12-80 mm
M8	13.0 mm	8.0 mm	6 mm	800 MPa	1.220 MPa	16-100 mm
M10	16.0 mm	10.0 mm	8 mm	800 MPa	1.220 MPa	20-120 mm
M12	18.0 mm	12.0 mm	10 mm	800 MPa	1.220 MPa	25-150 mm
M16	24,0 mm	16.0 mm	14 mm	800 MPa	1.220 MPa	30-200 mm

Ori-si-o tẹle ratio ọrọ fun ipata oniru: kan ti o tobi iyipo ori yoo fun awọn ti a bo kan ọrọ, kekere-wahala dada lati mnu si, nigba ti jin iho recess ni julọ ti a bo-lominu ni agbegbe ti gbogbo dabaru - o jẹ ibi ti ipata akọkọ ku ati ibi ti a tinrin tabi pipe fiimu fa awọn boluti lati gba.

Dacromet ti a bo hexagonal iyipo ori dabaru

3. Fifi sori: Torque, Preload, ati Coating Interaction

Boluti ti ko ni ipata jẹ asan ti apapọ ba tú. Tabili 2 n funni ni iyipo apejọ fun kilasi 8.8 ati awọn skru ori iho iho 10.9 pẹlu bo Dacromet (μ ≈ 0.14).

Opo	Kilasi 8.8 Torque	Kilasi 8.8 iṣaju	Kilasi 10.9 Torque	Kilasi 10.9 iṣaju
M5	6.5 Nm	4.0 kN	9.0 Nm	5.6 kN
M6	11.5 N·m	5.7 kN	16.0 N·m	8.0 kN
M8	28.0 N·m	10.4 kN	39.0 N·m	14.6 kN
M10	55.0 N·m	16.5 kN	78.0 N · m	23.1 kN
M12	96.0 N · m	24.0 kN	135 N·m	33.6 kN
M16	240 N·m	45.0 kN	335 N·m	63.0 kN

Lo bọtini ti o tọ.Bọtini Allen ti o wọ tabi ti ko ni iwọn jẹ ibajẹ iho ati ṣiṣafihan irin igboro - aaye gangan nibiti ibajẹ ti bẹrẹ.
Ọwọ awọn counterbore.Awọn ijoko ori lori oju ti o ni kikun; a chamfered tabi bajẹ counterbore din olubasọrọ agbegbe ati ki o le kiraki awọn ti a bo fiimu labẹ fifuye.
Maṣe dapọ awọn ọna ṣiṣe ti a bolori kanna isẹpo lai tun-ayẹwo iyipo. Dacromet kan dabaru sinu nut itele ni o yatọ si edekoyede ju kan ti a bo dabaru sinu kan ti a bo nut.
Tun-yipo lẹhin pinpinlori awọn gasiketi asọ tabi awọn ile ṣiṣu; fiimu gbigbẹ ko ni rarako, ṣugbọn ohun elo ti o ni ihamọ le.

4. Ipari

Dacromet-coated hexagon socket head skru skru jẹ paati kekere ti o pinnu igbesi aye iṣẹ ti apejọ nla kan. Ori iyipo rẹ ati hexagon inu ṣe jiṣẹ ẹru dimole awọn ibeere ẹrọ ode oni; Awọn oniwe-sinkii-aluminiomu flake ti a bo gbà awọn egboogi-ipata išẹ ti ita gbangba, tona, ati transportation iṣẹ ibeere - lai hydrogen embrittlement, lai o tẹle re-kia kia, ati laisi galling ijiya ti irin alagbara, irin. Pato awọn Kọ ti tọ, yiyi o ti tọ, ati awọn boluti yoo outlast awọn kun lori ẹrọ ti o Oun ni papo.