Ite 8.8 dudu oxide ni ilopo-opin studs jẹ alabọde-giga asapo fasteners ifihan asapo lori mejeji opin pẹlu ohun unthreaded shank aarin. Wọn darapọ iṣẹ ṣiṣe ẹrọ ti o gbẹkẹle (agbara fifẹ 800 MPa), aabo ipata ti ọrọ-aje nipasẹ ibora iyipada Fe3O4 tinrin, ati fifi sori ẹrọ wapọ fun ẹrọ ile-iṣẹ, adaṣe, ati awọn ohun elo igbekalẹ.

1. Ite 8.8 Classification

Fun ISO 898-1, yiyan "8.8" tumọ si agbara fifẹ ti 800 MPa ati ipin ikore ti 0.8 (agbara ikore 640 MPa). Ti a ṣelọpọ lati inu irin alloy carbon alloy alabọde ti o pa ati-tempered, Ite 8.8 nfunni ni iwọntunwọnsi agbara-si-iye owo ti o dara julọ.

Tabili 1 - Awọn ohun-ini Mechanical Key (ISO 898-1)

2. Black Oxide dada itọju

Black oxide (Fe3O4) jẹ iyipada ti kemikali ti o nipọn 0.5-1.5 micrometers, ti a ṣe nipasẹ immersion ni iwẹwẹ nitrate ipilẹ gbigbona ni 140-150C. Ko dabi electroplating, o fa ko si onisẹpo ayipada ko si si hydrogen embrittlement. Nigbati a ba fi edidi di pẹlu epo idena ipata, o pese to awọn wakati 96 ti resistance sokiri iyọ.

Table 2 - Black Oxide Coating Properties

3. Double-Opin Okunrinlada Design

Okunrinlada meji-opin kan ni ipari tẹ ni kia kia (ti a fi sinu iho ti a tẹ) ati ipari eso kan (gba nut), ti a yapa nipasẹ shank ti ko ni itọka. Ipari ipari tẹ ni kia kia ni igbagbogbo 1.0-1.5d ati opin nut 2.0-3.0d, nibiti d jẹ iwọn ila opin.